Polyoxymethylene (POM), also known as acetal,[4]polyacetal, and polyformaldehyde, is an engineering thermoplastic used in precision parts requiring high stiffness, low friction, and excellent dimensional stability. Short-chained POM (chain length between 8 and 100 repeating units) is also better known as paraformaldehyde (PFA). As with many other synthetic polymers, polyoxymethylenes are produced by different chemical firms with slightly different formulas and sold as Delrin, Kocetal, Ultraform, Celcon, Ramtal, Duracon, Kepital, Polypenco, Tenac and Hostaform.
POM is characterized by its high strength, hardness and rigidity to −40 °C. POM is intrinsically opaque white because of its high crystalline composition but can be produced in a variety of colors.[1] POM has a density of 1.410–1.420g/cm3.[5]
Typical applications for injection-molded POM include high-performance engineering components such as small gear wheels, eyeglass frames, ball bearings, ski bindings, fasteners, gun parts, knife handles, and lock systems. The material is widely used in the automotive and consumer electronics industry. POM's electrical resistivity is 14×1015 Ω⋅cm making it a dielectric with a 19.5MV/m breakdown voltage.[2][6]
Circa 1952, research chemists at DuPont synthesized a version of POM,[9] and in 1956 the company filed for patent protection of the homopolymer,[10] forgetting to mention in the patent the term copolymer, opening thus the road to competitors. DuPont credits R. N. MacDonald as the inventor of high-molecular-weight POM.[11] Patents by MacDonald and coworkers describe the preparation of high-molecular-weight hemiacetal-terminated (~O−CH2OH) POM,[12] but these lack sufficient thermal stability to be commercially viable. The inventor of a heat-stable (and therefore useful) POM homopolymer was Stephen Dal Nogare,[13] who discovered that reacting the hemiacetal ends with acetic anhydride converts the readily depolymerizable hemiacetal into a thermally stable, melt-processable plastic.
In 1960, DuPont completed construction of a plant to produce its own version of acetal resin, named Delrin, at Parkersburg, United States.[14] Also in 1960, Celanese completed its own research. Shortly thereafter, in a limited partnership with the Frankfurt firm Hoechst AG, a factory was built in Kelsterbach, Hessen; from there, Celcon was produced starting in 1962,[15] with Hostaform joining it a year later. Both remain in production under the auspices of Celanese and are sold as parts of a product group now called 'Hostaform/Celcon POM.
To make polyoxymethylene homopolymer, anhydrousformaldehyde must be generated. The principal method is by reaction of the aqueous formaldehyde with an alcohol to create a hemiformal, dehydration of the hemiformal/water mixture (either by extraction or vacuum distillation) and release of the formaldehyde by heating the hemiformal. The formaldehyde is then polymerized by anionic catalysis, and the resulting polymer stabilized by reaction with acetic anhydride. Due to the manufacturing process, large-diameter cross-sections may have pronounced centerline porosity.[16] A typical example is DuPont's Delrin.
The polyoxymethylene copolymer replaces about 1–1.5% of the −CH2O− groups with −CH2CH2O−.[17]
To make polyoxymethylene copolymer, formaldehyde is generally converted to trioxane (specifically 1,3,5-trioxane, also known as trioxin).[18] This is done by acid catalysis (either sulfuric acid or acidic ion-exchange resins) followed by purification of the trioxane by distillation and/or extraction to remove water and other active hydrogen-containing impurities. Typical copolymers are Hostaform from Celanese and Ultraform from BASF.
The co-monomer is typically dioxolane, but ethylene oxide can also be used. Dioxolane is formed by reaction of ethylene glycol with aqueous formaldehyde over an acid catalyst. Other diols can also be used.
Trioxane and dioxolane are polymerized using an acid catalyst, often boron trifluoride etherate, BF3OEt2. The polymerization can take place in a non-polar solvent (in which case the polymer forms as a slurry) or in neat trioxane (e.g. in an extruder). After polymerization, the acidic catalyst must be deactivated and the polymer stabilized by melt or solution hydrolysis to remove unstable end groups.
Stable polymer is melt-compounded, adding thermal and oxidative stabilizers and optionally lubricants and miscellaneous fillers.
Typical applications for injection-molded POM include high-performance engineering components (e.g. gear wheels, ski bindings, yoyos, fasteners, lock systems). The material is widely used in the automotive and consumer electronics industry. There are special grades that offer higher mechanical toughness, stiffness or low-friction/wear properties.
POM is commonly extruded as continuous lengths of round or rectangular section. These sections can be cut to length and sold as bar or sheet stock for machining.
When supplied as extruded bar or sheet, POM may be machined using traditional methods such as turning, milling, drilling etc. These techniques are best employed where production economics do not merit the expense of melt processing. The material is free-cutting, but does require sharp tools with a high clearance angle. The use of soluble cutting lubricant is not necessary, but is recommended.
POM sheets can be cut cleanly and accurately using an infrared laser, such as in a CO2laser cutter.
Because the material lacks the rigidity of most metals, care should be taken to use light clamping forces and sufficient support for the work piece.
As can be the case with many polymers, machined POM can be dimensionally unstable, especially with parts that have large variations in wall thicknesses. It is recommended that such features be "designed-out" e.g. by adding fillets or strengthening ribs. Annealing of pre-machined parts before final finishing is an alternative. A rule of thumb is that in general, small components machined in POM suffer from less warping.
POM is typically very difficult to bond, with the copolymer typically responding worse to conventional adhesives than the homopolymer.[24] Special processes and treatments have been developed to improve bonding. Typically these processes involve surface etching, flame treatment, using a specific primer/adhesive system, or mechanical abrasion.
Typical etching processes involve chromic acid at elevated temperatures. DuPont uses a patented process for treating acetal homopolymer called satinizing that creates a surface roughness sufficient for micromechanical interlocking. There are also processes involving oxygen plasma and corona discharge.[25][26] In order to get a high bond strength without specialized tools, treatments, or roughening, one can use Loctite 401 prism adhesive combined with Loctite 770 prism primer to get bond strengths of ~1700psi.[24]
Once the surface is prepared, a number of adhesives can be used for bonding. These include epoxies, polyurethanes, and cyanoacrylates. Epoxies have shown 150–1,050 psi (1,000–7,200 kPa)[24] shear strength. Cyanoacrylates are useful for bonding to metal, leather, rubber, cotton, and other plastics.
Solvent welding is typically unsuccessful on acetal polymers, due to the excellent solvent resistance of acetal.[citation needed]
Thermal welding through various methods has been used successfully on both homopolymer and copolymer.[27]
A fountain pen with a polyoxymethylene body and capMechanical gears, sliding and guiding elements, housing parts, springs, chains, screws, nuts, fan wheels, pump parts, valve bodies.
Vehicle: fuel sender unit, light/control stalk/combination switch (including shifter for light, turn signal), power windows, door lock systems, articulated shells.
Model: model railway parts, such as trucks (bogies) and hand rails (handle bars). POM is tougher than ABS, comes in bright translucent colors, and is not paintable.
Dunlop "Delrin 500" guitar pickConstruction: structural glass - pod holder for point
Packaging: aerosol cans, vehicle tanks.
Pens: used as the material for pen bodies and caps
Sports: paintball accessories. It is often used for machined parts of paintball markers that do not require the strength of aluminium, such as handles and reciprocating bolts. POM is also used in airsoft guns to reduce piston noise.
Longboarding: puck material for slide gloves help the rider touch the road and lean on their hand to slow down, stop, or perform tricks.
Acetal resins are sensitive to acidhydrolysis and oxidation by agents such as mineral acid and chlorine.[36] POM homopolymer is also susceptible to alkaline attack and is more susceptible to degradation in hot water. Thus low levels of chlorine in potable water supplies (1–3 ppm) can be sufficient to cause environmental stress cracking, a problem experienced in both the US and Europe in domestic and commercial water supply systems. Defective mouldings are most sensitive to cracking, but normal mouldings can succumb if the water is hot. Both POM homopolymer and copolymer are stabilized to mitigate these types of degradation.
In chemistry applications, although the polymer is often suitable for the majority of glassware work, it can succumb to catastrophic failure. An example of this would be using the polymer clips on hot areas of the glassware (such as a flask-to-column, column-to-head or head-to-condenser joint during distillation). As the polymer is sensitive to both chlorine and acid hydrolysis, it may perform very poorly when exposed to the reactive gases, particularly hydrogen chloride (HCl). Failures in this latter instance can occur with seemingly unimportant exposures from well sealed joints and do so without warning and rapidly (the component will split or fall apart). This can be a significant health hazard, as the glass may open or smash. Here, PTFE or a high-grade stainless steel may be a more appropriate choice.
In addition, POM can have undesirable characteristics when burned. The flame is not self-extinguishing, shows little to no smoke, and the blue flame can be almost invisible in ambient light. Burning also releases formaldehyde gas, which irritates nose, throat, and eye tissues.
^US 2998409, Nogare, Stephen Dal & Punderson, John Oliver, "Polyoxymethylene carboxylates of improved thermal stability", published 1961-08-29, assigned to E. I. Du Pont de Nemours and Co.